Microstructural evolution and mechanical characterization of a WC

Scientific Reports volume 12, Article number: 9822 (2022) Cite this article

1971 Accesses

10 Citations

5 Altmetric

Metrics details

High entropy alloys (HEAs) are a relatively new class of material that have shown the potential to exhibit excellent combinations of mechanical properties. Various microstructural modifications have been explored to further enhance their mechanical properties for use in demanding structural applications. The main focus of the present work is an investigation of the effect of adding varying amounts of hard ceramic material (WC) to a tough HEA matrix (CoCrFeNi) by arc melting under an argon atmosphere, including microstructural changes, and evaluation of the WC additions on mechanical properties. X-ray diffraction analysis of the HEA-WC composites showed the presence of both fcc and carbide phases. Scanning electron microscope investigations, including energy dispersive spectroscopy, reveal that chromium diffuses from the matrix and interacts with WC to form an alloyed carbide phase. The amount of alloyed carbide was found to increase with increasing amount of WC addition to the HEA matrix. Mechanical characterization revealed that hardness and yield strength of the HEA-WC composites increase with increasing amount of the carbide phase in the matrix. The hardness of HEA-20wt.% WC sample was found to be as high as 3.3 times (593 HV) the hardness of the base HEA (180 HV), while the yield strength increased from 278 MPa for the base HEA to 1098 MPa for the CoCrFeNi-20 wt.% WC composite. The investigated composites also showed excellent values of ductility (~ 50% strain for CoCrFeNi-10 wt% WC and ~ 20% strain for CoCrFeNi-20 wt% WC). It is therefore believed that ceramic-reinforced high entropy matrix composites have the potential to provide outstanding combinations of mechanical properties for demanding structural applications.

Strength and toughness are the two key properties required in structural materials for safe endurance of high loads. Increases in strength, however, are in many materials inevitably accompanied by some sacrifice in ductility, with a corresponding loss of toughness. Grain refinement of coarse-grained Ni metal to the nanoscale, for example, has been reported to lead to an increase in yield strength from just 53 MPa to 1.3 GPa, but at the cost of a severe decrease in ductility (to < 5%)1. A number of different attempts have been made to overcome this strength-ductility trade off. Some notable approaches that have been tried in this regard include development of heterogeneous nanostructures2 or hierarchical microstructures3,4, use of nano-precipitation strengthening5, austempering6, and spheroidization7, as well as alloy design to encourage either transformation induced plasticity (TRIP)8 or twinning induced plasticity (TWIP)9,10. Nevertheless, the strength- ductility tradeoff remains an outstanding issue and it increasingly seems that the mechanical properties of conventional alloys are approaching their capacity limits.

High entropy alloys (HEAs) form a relatively new class of material that are based on the simultaneous presence of four or five or more elements in equal amounts11,12. HEAs are characterized by the presence of four characteristic effects, namely configurational entropy, severe lattice distortion, sluggish diffusion and the cocktail effect11,13,14. These effects are considered to be responsible for better combinations of properties in comparison to conventional alloys, including outstanding thermal stability, corrosion resistance, and fatigue strength, as well as superplastic elongation and better mechanical properties even at cryogenic temperatures12,15,16,17,18,19,20,21,22,23,24,25,26. HEAs have also shown the potential to exhibit enhanced combinations of strength and ductility. Excellent ductility can be achieved in fcc HEAs, albeit with limited strength, whereas high strength but limited ductility has been reported for bcc HEAs Different attempts have been carried out, therefore, to further enhance the strength-ductility combinations in HEAs by design of HEAs containing both fcc and bcc solid-solution phases, where some promising results have already been achieved27,28,29. Development of HEAs strengthened by interstitial solid-solutions has also been explored. Addition of nitrogen30, oxygen31 and carbon32,33 atoms into a HEA matrix has been reported to improve strength, but at the expense of limited ductility. HEAs utilizing the TRIP effect have also been developed in a quest for better combinations of mechanical properties8,34,35. Transformation of metastable phases under stress has in some cases been reported to improve the ability to resist fracture, however at present only a few systems have been shown to exhibit good results in this regard8,34. Development of a thin deformed layer and an undeformed core, connected by a gradient hierarchical microstructure36 in a HEA was also shown to improve ductility, but with only a small corresponding increase in strength. Additionally, eutectic HEAs, consisting of fine lamellae of hard and soft phases37,38, have also been developed by employing different alloy design strategies. The use of such eutectic microstructures in HEAs has shown promising results. Design and control of eutectic microstructures in HEAs is, however, an extremely difficult task, due to the simultaneous presence of multiple elements.

The idea of reinforcing a HEA matrix with a ceramic phase in order to obtain better combinations of mechanical properties has also recently emerged. Development of such HEA composites has been tried both by ex-situ additions of discrete ceramic particles and also by in-situ formation of ceramic phases in an HEA matrix39. The main focus in the case of HEA composites based on a fcc matrix is to improve the yield and tensile strength without compromising ductility, based on the idea that a fcc matrix may provide good toughness while the ceramic phase contributes to high strength. In a recent study, a CoCrFeMnNi fcc HEA was reinforced with TiC and TiN particles, resulting in a significant improvement in mechanical properties40,41,42. Similarly, in-situ formation of TiC has also been explored in the (CoCrFeNi)AlxCuy HEA system43. Improvement in the plasticity and fracture toughness of bcc HEAs may also help towards the goal of obtaining better combinations of strength and ductility. For example, addition of TiC and TaC to the Mo0.5NbHf0.5ZrTi bcc HEA44,45 resulted in the development of a eutectic microstructure and the presence of metal carbide precipitates, with the bcc phase in the microstructure helped to obtain high strength combined with good ductility.

In the present study we focus on development of ceramic-reinforced HEA composites with a fcc matrix as part of a wider search of materials with improved combinations of strength and ductility. The CoCrFeNi system, as one of the most widely studied fcc HEAs, was selected as the matrix material for the study. For the ceramic phase WC is chosen, due to is relatively good toughness and its widespread use as a high density ceramic material in demanding applications. Using these starting materials CoCrFeNi-WC composites were prepared by an arc melting process. The evolution of microstructure and crystal structure were studied as a function of WC weight fraction, together with an investigation of the mechanical properties of the HEA-ceramic composites.

High purity elemental powders of cobalt, chromium, iron, and nickel, together with tungsten carbide (WC) ceramic powder (purity > 99.95%) were used as raw materials. Metal powders with varying additions of WC powder (0, 5, 10, or 20 wt%) were mixed in an agate mortar, followed by arc melting under a high-purity argon atmosphere to produce HEA composite buttons of 20 g weight. Each composition was re-melted five times, with samples flipped over after each melting to ensure chemical homogeneity. Measurements taken before and after melting showed a weight difference of less than 0.5%. Sectioning of the HEA composite buttons for characterization of mechanical properties, as well as for investigation of the phase composition, microstructure and chemical analysis, was carried out using electrical discharge wire cutting. Samples for microstructural evaluation were carefully prepared using standard metallographic preparation procedures and then etched with aqua regia. The microstructure was examined both using an optical microscope (OPTIKA-600) and a scanning electron microscope (SEM; JEOL JSM-6490LA and VEGA-3), equipped with a Bruker energy-dispersive X-ray spectroscopy (EDS) system. Crystal structure characterization of the composites was carried out using an X-ray diffraction (XRD) system, operated with a CuKα source at a step size of 0.04°. Vickers microhardness measurements were performed on polished cross-sectional surfaces using a 136° Vickers diamond pyramid indenter. The Vickers hardness (HV0.3) was measured under 300 N force using a 15 s dwell time. Room temperature compression testing was performed using a SHIMADZU universal testing machine with tests carried out at an initial strain rate of 1 × 10–3 s−1.

This study was funded by the Higher Education Commission of Pakistan (HEC-NRPU Project # 6019).

A sample of HEA matrix without WC addition was characterized prior to investigation of the HEA-ceramic composites to provide a reference material. An example SEM micrograph of the as-cast CoCrFeNi HEA is shown in Fig. 1a, together with accompanying EDS analysis at selected locations in Fig. 1b. The similarity of the EDS results in different locations confirms the chemical homogeneity of the single phase HEA. The XRD pattern of the base CoCrFeNi HEA, shown in Fig. 1c, also confirms that the base alloy was a single-phase fcc solid solution, in good agreement with the SEM microstructural observations.

Characterization of the base CoCrFeNi HEA: (a) SEM micrograph, (b) EDS analysis of the three regions labelled in (a), and (c) XRD pattern showing the single fcc phase composition.

XRD patterns of HEA composites prepared by arc melting under argon atmosphere using 5, 10 and 20 wt% of WC are shown in Fig. 2, where the data for the single phase HEA over the same 2θ range are also reproduced for reference. The XRD data clearly show the presence of peaks corresponding to the fcc phase, as well from an alloyed carbide phase. No peaks corresponding to the presence of the pure WC were observed. The chemical affinity of chromium for carbon is much higher than the affinity of W for carbon (the Gibbs free energies of Cr23C6, Cr7C3 and Cr3C2 are − 343.9 kJ/mol, − 144.4 kJ/mol, − 72.3 kJ/mol, respectively46). It is therefore assumed that chemical interaction of WC and chromium takes place during melting, resulting in disintegration of the WC and formation of chromium carbides. Scanning electron microscopy and EDS analysis were carried out to further investigate this hypothesis and to evaluate the effect of WC additions on the microstructure of the CoCrFeNi HEA phase. Example SEM images of the high entropy composites with initial WC contents of 5, 10, and 20 wt% are shown in Fig. 3.

X-ray diffraction patterns of the CoCrFeNi-WC composites together with data for the single phase CoCrFeNi HEA.

Example scanning electron micrographs of composite samples prepared from (a) CoCrFeNi-5 wt% WC (b) CoCrFeNi-10 wt% WC (c) CoCrFeNi-20 wt% WC. A eutectic microstructure consisting of an alloyed carbide phase (white) and a matrix phase (grey) can be seen, with an obvious increase in the eutectic phase volume fraction with increasing WC addition.

The SEM observations revealed the presence of a two phase microstructure, seen in the micrographs of Fig. 3 as grey matrix phase and lighter alloyed carbide phase (referred to in the following as white, though depending on SEM conditions this can also appear as light grey). The presence of a eutectic microstructure (consisting of a dark grey phase and white phase) is also seen at grain boundaries in the HEA-5wt%WC alloy (Fig. 3a). The amount of the eutectic phase was found to increase with increasing amount of WC addition.

Example chemical compositions of both the matrix and carbide regions in the CoCrFeNi-20 wt% WC alloy, as determined from EDS measurements, are shown in Fig. 4a,b. EDS analysis of the matrix (typified by position A in Fig. 4a) revealed more or less equiatomic concentrations of Co, Fe, and Ni, with a significant decrease in the amount of chromium as compared to the reference alloy (without WC addition). A small amount of W was also found in the matrix. Chemical analysis of the phase with white contrast (e.g., position B in Fig. 4a) showed relatively high amounts of Cr and W, consistent with diffusion of chromium from the matrix and chemical interaction with WC. This white phase was identified as an alloyed carbide, on the basis that the relative intensity of the peaks corresponding to an alloyed carbide phase in the XRD patterns also increased with increasing amount of WC addition in the HEA-ceramic composite.

(a) SEM image and (b) EDS analysis of the CoCrFeNi-20 wt% WC composite.

Based on these observations it is believed that during melting interaction between WC and the HEA components, especially Cr, takes place, leading to the formation of an alloyed carbide phase. As a result the W becomes partially dissolved in the matrix and partially dissolved in the carbide phase. A comparison of the SEM images shown in Fig. 3 also reveals that addition of WC leads to a grain size refinement, both in the case of the 5 wt% WC composite and also for the higher wt% composites, as a result of the formation of the eutectic and alloy carbide phases. The volume fraction of the alloy carbide phase increases with increasing amount of WC addition, with a corresponding decrease in grain size A slight shift of the fcc peaks in the HEA-WC composites towards the left for the 5 wt% WC and 10 wt% WC alloys (in comparison to the base HEA), despite the outward diffusion of chromium, is explained by the fact that W, with large atomic size, becomes dissolved in the matrix. For the 20 wt% WC alloy a large amount of carbide phase is formed. As a result the effect on lattice parameter of outward diffusion of chromium from the fcc matrix dominates over that from addition of W to the matrix, resulting in a slight shift of the fcc peak to the right.

The effect of the aforementioned microstructural changes on the mechanical properties of the HEA composites was evaluated by use of hardness and compression testing. The results of the hardness measurements are shown in Fig. 5a. The hardness of the base HEA was found to be 180 HV, increasing linearly with increasing amount of WC addition. The hardness of the HEA-20 wt% WC sample was found to be as high as 3.3 times (593 HV) the hardness of the base HEA. The increase in hardness was attributed both to lattice distortion resulting from diffusion of W into the matrix, as well as to the increase in the amount of the alloy carbide phase. The yield strength and ductility of the HEA-WC composites were evaluated by compression testing. Engineering stress–strain curves of HEA composites are shown in Fig. 5b, while the variation of yield strength (defined as the 0.2% proof stress) as a function of the amount of added WC in the master alloy is shown in Fig. 5c.

Mechanical properties of the HEA–WC composites: (a) variation of hardness as a function of amount of added WC (loading fraction); (b) compressive stress–strain curves; and (c) variation of yield strength (0.2% proof stress) as a function of amount of added WC.

Compression test curves for the CoCrFeNi HEA and CoCrFeNi-5 wt% WC composites show a concave appearance, while compression curves of the CoCrFeNi-10 wt% WC composite and CoCrFeNi-20 wt% WC composite exhibit a convex shape. A stress–strain with concave appearance is typically characteristic of the activation of either twinning or TRIP effects, while dislocation glide-dominated deformation results typically in a convex profile47,48. The observations therefore suggest a change in the deformation mode as the amount of added WC in the base HEA (master alloy) increases to 10% and above. The variation of yield strength as a function of amount of WC in the HEA composite is shown in Fig. 5c. The yield strength increases from 278 MPa for the base HEA to 1098 MPa for the CoCrFeNi-20 wt% WC composite, mirroring the increase observed from the hardness measurements. In addition to the significant increase in the yield strength observed, the composites were found also to retain excellent values of ductility. In particular the HEAs with 10 wt% WC and 20 wt% WC addition exhibited good elongation before fracture, reaching values of about ~ 50% and ~ 20% strain, respectively, along with high values of compressive strength. An increase in strength resulting from the WC additions without significant decrease in ductility was attributed to three different aspects of the microstructural changes in the HEA composites: (1) grain size refinement, (2) dispersion strengthening, and (3) the presence of a fine eutectic microstructure consisting of hard (carbides) and soft (fcc) phases.

Grain size refinement is attributed to the promotion of heterogenous nucleation during solidification by chromium carbides, formed as a result of disintegration of WC and interaction of the released C with Cr in the HEA matrix. A fine grain size is known to help with slip homogenization, promoting ductility, and also leads directly to strengthening via the Hall–Petch relationship. Enhanced work hardening in the alloy due to twinning also extends the necking stage, thereby enhancing ductility29. Alloyed carbide particles are expected also be present in the form of fine particles dispersed in the matrix phase. The presence of such fine carbides can be expected to lead to an increase in work-hardening capability through dislocation-particle interactions, as well as to promotion of slip homogeneity within each grain. The latter results in a delayed build-up of dislocation pile-up stresses at the coarse grain boundary carbides, contributing also to the improved balance of strength and ductility in the composites. Similarly the presence of a mesoscale distribution of the larger alloy carbides (as seen in Figs. 3 and 4) can be expected to promote an increase during deformation in the density of geometrically necessary dislocations in regions of the HEA matrix adjacent to the harder alloy carbides. A difference in the both the thermal expansion coefficients and the elastic modulii between the HEA matrix and precipitated carbides has also been previously reported to enhance composite properties40,49.

The development of a fine-scale eutectic microstructure, consisting of a hard (carbide) phase and a softer fcc phase, also directly contributes to an improvement in strength. Moreover, the micrometer-scale distribution of this eutectic phase, in particular in the 10% WC composite sample, results in a hierarchical hard/soft microstructure, benefitting both the strength and plasticity of the HEA-WC composites. It can be noted also that the presence of the eutectic phase can also help to reduce castability problems, by reducing the possibility for deleterious segregation.

The results of the present study show that ceramic-reinforced high entropy matrix composites can help to achieve the goal of attaining alloys with improved combinations of strength and ductility. The selection of the ceramic reinforcement for a particular HEA matrix, and of the accompanying processing route is, however, very important in this regard. Among the elements present in the CoCrFeNi matrix, chromium has the strongest affinity for the formation of carbides, and therefore results in disintegration of WC due to the negative enthalpy for Cr carbide formation46,50. In a previous study the same HEA matrix was reinforced with WC by spark plasma sintering of mechanically alloyed HEA/WC powder. In that work the presence of four different phases, namely a fcc matrix phase, WC, M23C6-type carbides and M7C3-type carbides, was found50. The strength of the as-sintered composites was high, but the composite suffered from low ductility, as a result of the formation of the various carbides. This was attributed to the presence of a process control agent as well as other contamination during mechanical alloying. In another study, the CoCrFeNi HEA system was reinforced with WC and applied as a coating on a steel substrate by vacuum hot-press sintering, with the goal of improving the surface properties of the steel. The resulting microstructure contained some WC as well as other carbides, all of which were uniformly distributed in the fcc phase51, and an improvement in both hardness and wear resistance was found. Taken together with the present study, these results indicate that the same combination of ceramic reinforcement phase and HEA system can lead to the formation of different types of microstructure depending on the applied processing route, resulting in a modification of the mechanical properties to a different extent in each case.

Ceramic reinforced HEA-matrix composites have been successfully prepared by addition of WC to a CoCrFeNi matrix through an arc melting route.

Chemical analysis and crystal structure analysis reveal interaction of WC with the HEA components. Specifically, chromium combines with decomposed WC to form an alloyed carbide phase in the fcc HEA matrix.

Microstructural investigations reveal the presence of alloyed carbides both at the grain boundaries and as part of a eutectic phase. The amount of alloyed carbide phase was found to increase with increasing amount of WC addition in the HEA composite.

Mechanical characterization reveals that the hardness and yield strength of the HEA composites increase with increasing amount of carbide phase in the matrix. The hardness of the HEA-20 wt% WC composite sample (593 HV) was found to be as high as 3.3 times that of the base HEA (180 HV), while the yield strength increased from 278 MPa for the base HEA to 1098 MPa for the CoCrFeNi-20 wt% WC composite.

The HEA composites retain excellent ductility to failure (~ 50% strain for CoCrFeNi-10 wt% WC and ~ 20% strain for CoCrFeNi-20 wt% WC). It is therefore believed that development of HEA composites can help in achieving alloys with improved combinations of strength, ductility and toughness.

The data used to support the findings of this study are included within the article.

Wu, X. et al. Nanodomained nickel unite nanocrystal strength with coarse-grain ductility. Sci. Rep. 5, 11728 (2015).

Article ADS PubMed PubMed Central Google Scholar

Ma, E. & Zhu, T. Towards strength-ductility synergy through the design of heterogeneous nanostructures in metals. Mater. Today 20(6), 323–331 (2017).

Article CAS Google Scholar

Dang, B. et al. Breaking through the strength-ductility trade-off dilemma in an Al-Si-based casting alloy. Sci. Rep. 6, 30874 (2016).

Article ADS CAS PubMed PubMed Central Google Scholar

Liddicoat, P. V. et al. Nanostructural hierarchy increases the strength of aluminium alloys. Nat. Commun. 1, 63 (2010).

Article ADS PubMed CAS Google Scholar

Liu, G. et al. Nanostructured high-strength molybdenum alloys with unprecedented tensile ductility. Nat. Mater. 12(4), 344–350 (2013).

Article ADS CAS PubMed Google Scholar

Bilal, M. M. et al. Effect of austempering conditions on the microstructure and mechanical properties of AISI 4340 and AISI 4140 steels. J. Market. Res. 8(6), 5194–5200 (2019).

MathSciNet CAS Google Scholar

Wang, Y. et al. A low-alloy high-carbon martensite steel with 2.6 GPa tensile strength and good ductility. Acta Mater. 158, 247–256 (2018).

Article ADS CAS Google Scholar

Li, Z. et al. Metastable high-entropy dual-phase alloys overcome the strength-ductility trade-off. Nature 534(7606), 227–230 (2016).

Article ADS CAS PubMed Google Scholar

Haase, C. & Barrales-Mora, L. A. Influence of deformation and annealing twinning on the microstructure and texture evolution of face-centered cubic high-entropy alloys. Acta Mater. 150, 88–103 (2018).

Article ADS CAS Google Scholar

Wei, Y. et al. Evading the strength-ductility trade-off dilemma in steel through gradient hierarchical nanotwins. Nat. Commun. 5, 3580 (2014).

Article ADS PubMed CAS Google Scholar

Yeh, J.-W. Recent progress in high-entropy alloys. Annales de Chimie Science des Matériaux 31(6), 633–648 (2006).

Article CAS Google Scholar

Miracle, D. et al. Exploration and development of high entropy alloys for structural applications. Entropy 16(1), 494–525 (2014).

Article ADS CAS Google Scholar

Yeh, J.-W. Alloy design strategies and future trends in high-entropy alloys. JOM 65(12), 1759–1771 (2013).

Article CAS Google Scholar

Tong, C.-J. et al. Microstructure characterization of AlxCoCrCuFeNi high-entropy alloy system with multiprincipal elements. Metall. Mater. Trans. A. 36(4), 881–893 (2005).

Article Google Scholar

Shahmir, H. et al. Evidence for superplasticity in a CoCrFeNiMn high-entropy alloy processed by high-pressure torsion. Mater. Sci. Eng. A 685, 342–348 (2017).

Article CAS Google Scholar

Zhang, Y. et al. Microstructures and properties of high-entropy alloys. Prog. Mater. Sci. 61, 1–93 (2014).

Article CAS Google Scholar

Gludovatz, B. et al. A fracture-resistant high-entropy alloy for cryogenic applications. Science 345(6201), 1153–1158 (2014).

Article ADS CAS PubMed Google Scholar

Senkov, O. et al. Development of a refractory high entropy superalloy. Entropy 18(3), 102 (2016).

Article ADS CAS Google Scholar

Senkov, O. N. et al. Development and exploration of refractory high entropy alloys—A review. J. Mater. Res. 33(19), 3092–3128 (2018).

Article ADS CAS Google Scholar

Gali, A. & George, E. P. Tensile properties of high- and medium-entropy alloys. Intermetallics 39, 74–78 (2013).

Article CAS Google Scholar

Yeh, J.-W. et al. Nanostructured high-entropy alloys with multiple principal elements: Novel alloy design concepts and outcomes. Adv. Eng. Mater. 6(5), 299–303 (2004).

Article CAS Google Scholar

Tsai, M.-H. & Yeh, J.-W. High-entropy alloys: A critical review. Mater. Res. Lett. 2(3), 107–123 (2014).

Article CAS Google Scholar

Tang, Z. et al. Alloying and processing effects on the aqueous corrosion behavior of high-entropy alloys. Entropy 16(2), 895–911 (2014).

Article ADS CAS Google Scholar

Chen, Y. Y. et al. Microstructure and electrochemical properties of high entropy alloys—A comparison with type-304 stainless steel. Corros. Sci. 47(9), 2257–2279 (2005).

Article CAS Google Scholar

Chou, Y. L. et al. Pitting corrosion of the high-entropy alloy Co1.5CrFeNi1.5Ti0.5Mo0.1 in chloride-containing sulphate solutions. Corros. Sci. 52(10), 3481–3491 (2010).

Article CAS Google Scholar

Kao, Y.-F. et al. Electrochemical passive properties of AlxCoCrFeNi (x = 0, 0.25, 0.50, 1.00) alloys in sulfuric acids. Corros. Sci. 52(3), 1026–1034 (2010).

Article CAS Google Scholar

Tang, Z. et al. Designing high entropy alloys with dual fcc and bcc solid-solution phases: Structures and mechanical properties. Metall. Mater. Trans. A. 50(4), 1888–1901 (2019).

Article CAS Google Scholar

Zhang, T. et al. Transformation-enhanced strength and ductility in a FeCoCrNiMn dual phase high-entropy alloy. Mater. Sci. Eng. A 780, 139182 (2020).

Article CAS Google Scholar

Xu, D. et al. A critical review of the mechanical properties of CoCrNi-based medium-entropy alloys. Microstructures 2, 2022001 (2022).

Google Scholar

Moravcik, I. et al. Yield strength increase of a CoCrNi medium entropy alloy by interstitial nitrogen doping at maintained ductility. Scripta Mater. 178, 391–397 (2020).

Article CAS Google Scholar

Lei, Z. et al. Enhanced strength and ductility in a high-entropy alloy via ordered oxygen complexes. Nature 563, 546–550 (2018).

Article ADS CAS PubMed Google Scholar

Shang, Y. Y. et al. Solving the strength-ductility tradeoff in the medium-entropy NiCoCr alloy via interstitial strengthening of carbon. Intermetallics 106, 77–87 (2019).

Article CAS Google Scholar

Wang, Z. et al. The effect of interstitial carbon on the mechanical properties and dislocation substructure evolution in Fe40.4Ni11.3Mn34.8Al7.5Cr6 high entropy alloys. Acta Mater. 120, 228–239 (2016).

Article ADS CAS Google Scholar

Liu, J. et al. Excellent ductility and serration feature of metastable CoCrFeNi high-entropy alloy at extremely low temperatures. Sci. China Mater. 62(6), 853–863 (2018).

Article CAS Google Scholar

George, E. P., Curtin, W. A. & Tasan, C. C. High entropy alloys: A focused review of mechanical properties and deformation mechanisms. Acta Mater. 188, 435–474 (2020).

Article ADS CAS Google Scholar

Hasan, M. N. et al. Simultaneously enhancing strength and ductility of a high-entropy alloy via gradient hierarchical microstructures. Int. J. Plast 123, 178–195 (2019).

Article CAS Google Scholar

Shi, P. et al. Enhanced strength-ductility synergy in ultrafine-grained eutectic high-entropy alloys by inheriting microstructural lamellae. Nat. Commun. 10(1), 489 (2019).

Article ADS CAS PubMed PubMed Central Google Scholar

Mukarram, M., Mujahid, M. & Yaqoob, K. Design and development of CoCrFeNiTa eutectic high entropy alloys. J. Market. Res. 10, 1243–1249 (2021).

CAS Google Scholar

Stepanov, N. D. et al. Effect of carbon content and annealing on structure and hardness of the CoCrFeNiMn-based high entropy alloys. J. Alloy. Compd. 687, 59–71 (2016).

Article CAS Google Scholar

Yim, D. et al. Fabrication and mechanical properties of TiC reinforced CoCrFeMnNi high-entropy alloy composite by water atomization and spark plasma sintering. J. Alloy. Compd. 781, 389–396 (2019).

Article CAS Google Scholar

Amar, A. et al. Additive manufacturing of high-strength CrMnFeCoNi-based high entropy alloys with TiC addition. Intermetallics 109, 162–166 (2019).

Article CAS Google Scholar

Li, B. et al. Fine-structured CoCrFeNiMn high-entropy alloy matrix composite with 12 wt% TiN particle reinforcements via selective laser melting assisted additive manufacturing. Mater. Lett. 252, 88–91 (2019).

Article CAS Google Scholar

Fan, Q. C., Li, B. S. & Zhang, Y. The microstructure and properties of (FeCrNiCo)Al Cu high-entropy alloys and their TiC-reinforced composites. Mater. Sci. Eng. A 598, 244–250 (2014).

Article CAS Google Scholar

Wei, Q. et al. Designing high entropy alloy-ceramic eutectic composites of MoNbRe0.5TaW(TiC)x with high compressive strength. J. Alloys Compd. 818, 152846 (2020).

Article CAS Google Scholar

Wei, Q. et al. Microstructure evolution, mechanical properties and strengthening mechanism of refractory high-entropy alloy matrix composites with addition of TaC. J. Alloy. Compd. 777, 1168–1175 (2019).

Article CAS Google Scholar

Kleykamp, H. Thermodynamic studies on chromium carbides by the electromotive force q (emf) method. J. Alloy. Compd. 321, 138–145 (2001).

Article CAS Google Scholar

Zhang, H. et al. Compressive deformation behavior of AZ31Mg alloy containing 10–12 extension twins at different temperature. Met. Mater. Int. 25(5), 1170–1181 (2019).

Article CAS Google Scholar

Kaviani, M. et al. Relationship between mechanical properties, microstructure and texture evaluations during hot deformation of AZ63 magnesium alloy. Mater. Res. Express 6(6), 066509 (2019).

Article ADS CAS Google Scholar

Casati, R. & Vedani, M. Metal matrix composites reinforced by nano-particles—A review. Metals 4(1), 65–83 (2014).

Article CAS Google Scholar

Zhou, R. et al. Microstructures and wear behaviour of (FeCoCrNi)1–x(WC)x high entropy alloy composites. Int. J. Refract Met. Hard Mater. 75, 56–62 (2018).

Article CAS Google Scholar

Xu, J. et al. Microstructure and properties of CoCrFeNi(WC) high-entropy alloy coatings prepared using mechanical alloying and hot pressing sintering. Coatings 9(1), 16 (2018).

Article CAS Google Scholar

Download references

School of Chemical and Materials Engineering (SCME), National University of Sciences and Technology (NUST), H-12, Islamabad, Pakistan

Syed Waqas Hussain, M. Adil Mehmood & Khurram Yaqoob

Department of Materials Science and Engineering, Ghulam Ishaq Khan Institute of Engineering Sciences and Technology, Topi, Swabi, 23640, KPK, Pakistan

M. Ramzan Abdul Karim

Laboratory of Advanced Materials (MoE), School of Materials Science and Engineering, Tsinghua University, Beijing, 100084, China

Andy Godfrey

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

S.W.H. and M.A.M. performed experimental work and written the main manuscript. M.R.A.K. and A.G. provided raw materials and helped in explaining mechanical response of developed composites. K.Y. envisaged the topic, supervised the experimental work and finalized thesis draft manuscript.

Correspondence to Khurram Yaqoob.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Hussain, S.W., Mehmood, M.A., Karim, M.R.A. et al. Microstructural evolution and mechanical characterization of a WC-reinforced CoCrFeNi HEA matrix composite. Sci Rep 12, 9822 (2022). https://doi.org/10.1038/s41598-022-13649-5

Download citation

Received: 18 November 2021

Accepted: 15 April 2022

Published: 14 June 2022

DOI: https://doi.org/10.1038/s41598-022-13649-5

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

Scientific Reports (2022)

Journal of Materials Engineering and Performance (2022)

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.