Microstructural and nanoindentation study of TaN incorporated ZrB2 and ZrB2

Scientific Reports volume 12, Article number: 13765 (2022) Cite this article

796 Accesses

Metrics details

This study assessed the sinterability and microstructure of ZrB2-SiC-TaN and ZrB2-TaN ceramics. Spark plasma sintering at 2000 °C and 30 MPa for 5 min produced both ceramics. The relative density of ZrB2 ceramic containing TaN was 95.3%; the addition of SiC increased this value to 98.1%. SiC’s contribution to the elimination of ZrB2 surface oxides was the primary factor in the advancement of densification. The in situ formation of hexagonal boron nitride at the interface of TaN and ZrB2 was confirmed by high-resolution transmission electron microscopy, field emission-electron probe microanalyzer, X-ray diffractometry, and field emission scanning electron microscopy. Moreover, the in situ graphite might be produced as a byproduct of the SiC-SiO2 process, hence boosting the reduction of oxide compounds in the ternary system. The SiC compound had the highest hardness (29 ± 3 GPa), while the ZrB2/TaN interface exhibited the greatest values of elastic modulus (473 ± 26 GPa) and stiffness (0.76 ± 0.13 mN/nm).

Combining boron or carbon with a transition metal from the fourth or fifth group of the periodic table produces a category of substances known as ultra-high temperature ceramics (UHTCs) with a high melting point (> 3000 °C)1,2,3,4. Among the UHTCs, ZrB2 possesses a number of intriguing properties, including outstanding hardness, a high elastic modulus, and excellent thermal and chemical stability5,6,7,8. Its particular qualities make it a suitable material for crucibles, armors, thermal shields, leading edges, turbine blades, and other applications9,10,11,12. Additionally, ZrB2's strong electrical conductivity makes it an appropriate substance for the production of electrical discharge devices and electrodes13,14. However, ZrB2 exhibits poor sinterability due to its strong covalent bonds and low self-diffusion. In particular, low oxidation resistance at elevated temperatures and low fracture toughness have constrained the use of undoped ZrB2 composites15,16,17. A number of studies have attempted to overcome the aforementioned limitations by utilizing advanced sintering techniques for the manufacture of ZrB2 composites and/or integrating appropriate sintering additives into ZrB2 composites. In terms of the production process, researchers have shown that the use of advanced sintering techniques (such as spark plasma sintering (SPS)) can improve the densification behavior and mechanical properties of ZrB2-based ceramics in comparison to the typical powder metallurgy technique18,19,20. During the sintering procedure, the SPS process applies external pressure and sparking phenomenon to the powder particles, considerably reducing the sintering temperature and residence time21,22,23. Regarding secondary phases, the influence of different metallic binders and additives on the qualities of ZrB2 composites has been investigated24. Nguyen and colleagues evaluated the effect of sintering temperature on the consolidation behavior of ZrB2-SiC ceramics25. They incorporated 30 vol% SiC to ZrB2 matrix; sintering the samples under 10 MPa for 60 min at three different sintering temperatures (2050, 1850, and 1650 °C) using a hot-pressing technique. They demonstrated that fragmentation and particle rearrangement were two significant densification mechanism routes at 1650 °C, but diffusion was perhaps the most important mechanism path at 2050 °C. In addition, plastic deformation was identified as the predominant consolidation process at 1850 °C. Consequently, a nearly fully dense specimen was produced at a sintering temperature of 2050 °C; its relative density value was ~ 8% percent more than the density of the specimen produced at 1650 °C. High-resolution microstructural studies and X-ray diffractometry (XRD) analyses validated the inertness of ZrB2-SiC under the applied sintering conditions. Wu et al.26 produced ZrB2-SiC-BN ceramic via the reactive SPS from an initial composition of B4C, Si3N4, and ZrB2. Transmission electron microscopy (TEM) and scanning electron microscopy (SEM) evaluations demonstrated the development of nano- and micro-sized intergranular hexagonal boron nitride (hBN) during the SPS process. Although the impact of hBN on the average grain size of SiC was negligible, the increased amount of hBN could significantly refine the matrix of the final specimens. Nguyen et al.27 prepared ZrB2-SiC-AlN ceramics using hot-press technique at 10 MPa at 1900 °C for 120 min; the properties of the products was analyzed in terms of sintering behavior and microstructural features. AlN had a significant impact on the densification behavior of the prepared samples, resulting in ceramics that were nearly completely dense. The thermodynamic analysis, XRD results, and microstructural images all supported in situ production of graphite during hot pressing. In addition, the grains were generally fragmented trans-granularly in accordance with the fracture surfaces of the composites, indicating that the constituent particles were strongly bonded. Ahmadi and colleagues28 studied the ZrB2-SiC composites containing different amounts of Si3N4. They utilized hot-pressing as the sintering procedure at 1900 °C to achieve fully dense specimens. The reaction between the Si3N4 and B2O3 surface oxide led to the formation of hBN. Furthermore, carbon, ZrB2, and Si3N4, which were created during the pyrolysis of the phenolic resin addition, participated in the reaction, resulting in the in situ production of ZrC and hBN components.

The effect of TaN inclusion on the microstructure and sintering behavior of ZrB2 and ZrB2-SiC composites was studied in this study. Both specimens were sintered at a pressure of 30 MPa and a temperature of 2000 °C for 5 min using the SPS process. The produced ceramics were analyzed utilizing cutting-edge techniques, such as field emission-electron probe microanalyzer (FE-EPMA), field emission SEM (FESEM), high-resolution TEM (HRTEM), XRD, X-ray fluorescence (XRF), and X-ray photoelectron spectroscopy (XPS).

To produce ZrB2-TaN and ZrB2-SiC-TaN ceramics, TaN, SiC, and ZrB2 powders were admixed according to the compositions presented in Table S1. The particle size of TaN was ~ 5 µm and its purity was 99.5%. In addition, the purity of SiC and ZrB2 was 99.2% and 99.8%, respectively, and their particle sizes were ~ 3 µm and ~ 2 µm, respectively. The primary mixtures were dispersed in ethanol and ultrasonically blended for 80 min. The mixtures were completely dried on a magnetic hot plate and in an oven. The mixtures were then loaded into graphite molds and SPSed at 30 MPa and 2000 °C for 5 min. The surfaces of the prepared ceramics were polished using abrasive sheets (numbered 80 to 5000) after the graphite foils were removed. Using diamond grinding disks, the residual surface scratches on the composites were completely removed during the polishing process.

The relative density of the SPSed composites was calculated as the proportion of the bulk density to the theoretical density. The crystalline structures of the as-sintered ceramics were verified by XRD (Bruker D8 Advance) analyses. FESEM (Zeiss, SUPRA 55VP) and HRTEM (JEOL JEM-2100F) were utilized for microstructural evaluation, whereas FE-EPMA (JEOL JXA-8530F) was employed to evaluate elemental distribution of the produced composites. In addition, XPS (VG Scientifics, Sigma probe, Al K source) and XRF (Shimadzu, XRF-1800) were utilized to determine the probable elemental bonding and elemental composition of the ceramics. The HSC software (Version 6) was performed to analyze the likely chemical interactions occurring throughout the SPS procedure. The mechanical properties of the existing phases were measured using a nanoindenter (Agilent G200, USA) with a pyramid-shaped tip. Six impressions were made for each phase, and the pertinent information was retrieved from the load–displacement curves. The variables utilized were a loading rate of 40 mN/S for a holding time of 5 s and a maximum load of 400 mN. Each point's hardness was calculated using the Oliver-Pharr method (see the supporting information). Microhardness of the polished ceramics was measured using an Eseway Vickers tester with a diamond indenter under a load of 0.3 kg for 15 s. Using a Vickers hardness instrument, the testing settings for macrohardness were 30 kg load and 15 s.

Figure S1a–c depicts the FESEM images and XRD patterns of the as-purchased raw materials utilized in this investigation. According to the XRD patterns of ZrB2 and SiC powders, trace amounts of oxides (ZrO2 and SiO2) are present. Due to the high reactivity of Zr and Si elements with oxygen, it is frequently reported that ceramic and metallic powders contain surface oxides. Although ZrO2 oxide has been found as the only crystalline phase in ZrB2 powder, B2O3 cannot be avoided29. According to the literature, the evaporation–condensation kinetics during the sintering process of boride-based ceramics can induce B2O3 to contribute to grain coarsening30. In general, the presence of oxide species has a detrimental impact on the densification behavior of metallurgy-produced composites. Moreover, the existence of surface oxides causes excessive grain development, particularly in procedures requiring a long soaking time; they inhibit the formation of strong bonds between adjacent particles31,32. These phenomena diminish the mechanical properties of the manufactured composites. If the existence of a secondary phase results in oxide removal during the sintering process, the final product's quality will be greatly enhanced33,34. In addition, the SPS approach for removing some low-boiling point oxides (e.g., B2O3) has been proven effective35,36. In accordance with the XRD pattern of the TaN powder (Fig. S1c), a Ta2N-related peak was detected in addition to the TaN regular peaks.

Initially, the predicted relative densities of ZrB2-TaN and ZrB2-SiC-TaN ceramics were 95.3% and 98.1%, respectively. The ZrB2-TaN ceramic comprised 4.7% residual porosity, while the addition of SiC enhanced its relative density (~ 3%). This improvement is due to the higher sinterability of the ternary system in contrast to its binary equivalent. Figure 1 displays the XRD patterns of the produced ceramics containing and without SiC. The XRD pattern of ZrB2-TaN composite reveals two peaks associated with in situ produced hBN at 2θ = 26.5° and 54.6°. In addition to the hBN phase, the original ZrB2 and TaN components, no other compound was discernable in the XRD pattern.

XRD patterns of ZrB2-TaN and ZrB2-SiC-TaN ceramics.

A sample can be densified by multiple stages of the SPS procedure. First, a substantial quantity of electrical current flows via the powder particles' contact points, resulting in a local temperature increase. Such phenomena may occur in the ionization/evaporation/melting of surface oxides as well as some of the primary constituents; one of these phase changes is shown in Eq. (1), when the B2O3 is present in the initial ZrB2 particle melts. It should be noted that local temperature can rise as B2O3 evaporates in the initial stage37. In contrast to B2O3, the other surface oxides of ZrB2 (such as ZrO2) are stable at extremely high temperatures38. Endurance of ZrO2 during sintering has the greatest impact on the sinterability of the ZrB2-TaN composite. Indeed, there was no reductant in this system to convert this oxide into other compounds. However, the first mechanism of densification in ZrB2-based materials is particle fragmentation and rearrangement occurring at temperatures below 1750 °C. The pressure exerted has also a substantial effect on this mechanism. In addition, neck formation takes place at this stage due to the production of electric arcs and plasma between the powder particles. The second densification step in a ZrB2 system occurs at temperatures above 1750 °C, where plastic deformation predominates, resulting in the elimination of a significant fraction of accessible pores among the particles. When the temperature of sintering hits 2000 °C, the diffusion densification mechanism can be activated. At this point, there is a substantial potential that hBN might form in situ. Boron and nitrogen atoms may generate an in situ phase during diffusion of elements at the interface of the ZrB2 matrix and the TaN additive. Similar behavior was also observed in the TiB2-TiN system.

Figure 1 shows the XRD pattern of ZrB2-SiC-TaN composite. Similar to the ZrB2-SiC composite, the hBN phase was distinguishable in addition to the original phases. The densification mechanisms could be similar to those of the prior composite. The explanation for why the ternary system has a higher relative density than the binary system is addressed below. As previously indicated, the presence of surface oxides might impede consolidation. Based on Eq. (2), the presence of SiC in ZrB2 may result in oxide removal. Consequently, ZrO2 and B2O3 can both react with SiC to produce ZrB2 and other gaseous compounds.

The surface oxide of SiO2 can interact with SiC phase (Eq. 3), resulting in the formation of in situ graphite and gaseous SiO. No graphite could be observed in the relevant XRD pattern, indicating that the produced carbon engaged in other processes during the SPS procedure.

Both Eqs. (4) and (5) imply two plausible consumption reactions for the produced graphite. Carbon can interact chemically with ZrO2 and B2O3 to produce ZrB2 (Eq. 4). In contrast, carbon can react with some of the three oxide phases (ZrO2, SiO2, and B2O3) to generate ZrB2 and SiC in situ. In other words, the presence of SiC in ZrB2-TaN composite results in a chain of reactions in which the accessible surface oxides can be reduced to their original phases, hence enhancing the sinterability of the prepared composites. Figure 2 illustrates the dependence of Gibbs free energy (ΔG°) on temperature for Eqs. (2–5). All reactions had negative ΔG° values at 2000 °C, proving their feasibility at the sintering studied conditions.

Temperature dependency of ΔG° Eqs. (2–5).

Using XRF and XPS methods, the ternary structure of ZrB2-SiC-TaN ceramic was analyzed. The XRF study (Fig. 3) displays the elemental components of ZrB2-SiC-TaN ceramic (Zr, Ta, and Si), excluding those with low atomic mass (B, N, C, and O). Figure 4 exhibits the survey XPS analysis of ZrB2-SiC-TaN composite. Figure S2 represents the XPS analysis of C 1s; it reveals two peaks related with the C-Ta and C-Zr binding energies. Interfacial regions between ZrB2/SiC and TaN/SiC may create diffusion bonds. However, the XRD analyses were not sensitive enough to detect this effect.

XRF analysis of ZrB2-SiC-TaN ceramic.

XPS analysis of ZrB2-SiC-TaN ceramic.

Figures 5a and 6a demonstrate secondary electron FESEM images of the polished surfaces of ZrB2-TaN and ZrB2-SiC-TaN ceramics, respectively. It is clear that the ternary ceramic is less porous than its binary counterpart, which is consistent with the relative densities of the prepared ceramics. As previously described, the addition of SiC removes surface oxide species during the SPS process, hence improving the composites' sinterability.

(a and b) FESEM images of polished surface of ZrB2-TaN, and (c–f) the corresponding EPMA results.

(a and b) FESEM images of polished surface of ZrB2-SiC-TaN, and (c–h) the corresponding EPMA results.

Figure 5a,b demonstrate the FESEM images of the polished surface of ZrB2-TaN ceramic. The brightly colored phase is attributable to TaN, which is uniformly distributed within the ZrB2 matrix (gray-colored phase). According to the EPMA analysis (Fig. 5c–f), diffusion occurred between ZrB2 and TaN compounds at their interfaces. In such areas, the formation of solid solutions (Zr, Ta, and BN) is probable. By comparing Fig. 5d,f, it is possible to deduce that certain regions are rich in both boron and nitrogen. These sites can be seen clearly in Fig. 5d (red zones). This outcome is entirely consistent with the XRD analysis, specifically the in situ formation of the hBN phase as a result of an interaction between ZrB2 and TaN constituents at the interfaces. During the elemental diffusion between these two phases, some boron and nitrogen atoms may leave their places in the crystalline structures, contributing to the in situ production of hBN phase.

Figure 6a,b present FESEM micrographs of the polished surface of ZrB2-SiC-TaN ceramic. According to the EPMA analysis (Fig. 6c–h), the brilliant, dark, and gray phases are related with the TaN additive, the SiC reinforcement, and the ZrB2 matrix, respectively. The uniform distribution of TaN and SiC within the ZrB2 matrix indicates that the powder mixture was properly prepared. Similar to ZrB2-TaN ceramic, diffusion bonds are visible in the ZrB2-TaN and ZrB2-SiC interfacial regions. Furthermore, the formation of hBN is possible anywhere boron and nitrogen concentrations are high (Fig. 6d,h).

Figure 7a depicts TEM image of the interaction of two adjacent ZrB2 grains. It indicates that surface imperfections could be eliminated during the SPS process, allowing neighboring ZrB2 particles to form strong bonds. During the sintering process, certain dislocations are formed on both sides of the interfacial region due to the external pressure. The ZrB2/TaN interface appears neat (Fig. 7b). However, no visible grain boundary can be detected in the interfacial area image at high magnification (Fig. 7c). Consequently, these two phases may substantially diffuse together, producing a strong connection. The TEM micrograph and inverse fast Fourier transform (IFFT) image reveal the presence of dislocations within the TaN phase (Fig. 7d). In addition to external pressure (as a potential explanation for the production of dislocations), the mismatch between the thermal expansion coefficients of the available ingredients might lead to the formation of dislocations. This behavior would be more prominent during cooling stage of the sintering process.

(a–c) TEM and HRTEM images of ZrB2-SiC-TaN ceramics, and (d) the relevant IFFT image.

The ternary composite was examined utilizing the nanoindentation technique. Several load–displacement curves relating to different components of this composite are illustrated in Fig. 8. Due to the surface roughness, the calculation of hardness by Oliver-Pharr technique (see supporting information) leads to data propagation39,40. Hardness is significantly changed at the areas near the surface when the typical technique is applied to assess the penetration depth. For example, slippage of the indenter's tip may occur under low stresses on protrusions. Consequently, the achieved value for the projected area/indentation depth can be greater than the values obtained on surfaces with depressions or flat surfaces, resulting in lower hardness values. In short, small wrinkling may lead to varied hardness values considering a single phase. According to Table 1, the following is the sequence of hardness, elastic modulus, and stiffness values for ZrB2 and interfacial areas: SiC > ZrB2/SiC interface > ZrB2/TaN interface > ZrB2 > TaN (hardness), ZrB2/TaN interface > SiC > ZrB2 > TaN > ZrB2/SiC interface (elastic modulus), and ZrB2/TaN interface > SiC > TaN > ZrB2 > ZrB2/SiC interface (stiffness).

Nanoindentation results of ZrB2-SiC-TaN ceramic.

Elastic modulus is an intrinsic feature of the materials, which depends on binding forces of atoms and crystalline structure. The formation of strong bonds between adjacent phases enables the attainment of high mechanical characteristics for interface regions. ZrB2/SiC, for instance, could attain a hardness value of 25 GPa, which was greater than that of ZrB2. It is evident that SiC has a higher hardness compared to ZrB2; however, the interface hardness may be significantly lower than surrounding phases if a powerful bonding would not be formed.

The total mechanical work (Ut) and elastic energy (Ue) can be measured through calculating the area under each section of load–displacement curves. Afterward, Eq. (6) can be used to estimate the plastic energy (Up)41,42,43.

The plasticity index (Up/Ut) and elastic recovery (Ue/Ut) of ZrB2 and the noted interfaces are calculated. These values (two critical factors for any material) are presented in Table 1 and Fig. 9. Elastic recovery shows the resistivity of a compound against impact loading, while the plasticity index demonstrates the natural response for a component under plastic deformations41,42,43. Based on Fig. 9, ZrB2 had the most plastic recovery, while TaN exhibited the highest elastic recovery. Table 2 provides the calculated total energy, plastic energy, elastic energy, plasticity index, and elastic recovery of ZrB2-SiC-TaN ceramic phases.

Plasticity index and elastic recovery of different phases in ZrB2-SiC-TaN ceramic.

Elastic recovery and plasticity index (co-related to nanoindentation elastic and plastic energies) are characterization metrics for ceramic matrix and composites' mechanical performance. The elastic recovery (Ue/Utot) indicates the amount of energy that can be released after loading. Up/Utot is related to the inherent flexibility of the material. TaN has the lowest hardness, plasticity index (Up/Utot ratio), elastic modulus, and highest elastic recovery as demonstrated in Tables 1 and 2. In addition, despite its intermediate hardness (between SiC and TaN), the ZrB2 phase exhibits the elastic recovery of all investigated regions.

Table S2 illustrates the Vickers hardness values of the as-sintered composites. The microhardness of the SiC-free specimen was 15.2 GPa and its macrohardness was 14.3 GPa. However, after the introduction of SiC reinforcement, both of these values increased by ~ 15%. Residual porosity and composition appear to be the two most influential factors in the increases.

The sintering behavior and microstructural characteristics of ZrB2-TaN ceramics with and without SiC reinforcement were investigated. Under sintering conditions of 2000 °C, 30 MPa, and 5 min, spark plasma sintering was applied as the manufacturing procedure. The SiC-free ceramic had a residual porosity of 4.7%, while the SiC-containing ceramic had a residual porosity of 1.9%. Comparing ZrB2-SiC-TaN ceramic to a SiC-free specimen, the relative density of ZrB2-SiC-TaN ceramic improved most likely due to the influence of SiC on the elimination of surface oxides of ZrB2. In addition, it was confirmed that SiO2 may be reduced to graphite and gaseous phases by its parent phase (SiC). The generated graphite could also aid in the removal of further oxides during the SPS process. In addition, XRD measurements and microstructural observations showed the in situ synthesis of hBN in both binary and ternary composites as a result of the diffusion phenomenon at the interfaces of ZrB2 and TaN. Finally, the SiC phase exhibited the highest hardness value (29 ± 3 GPa), whereas the ZrB2/TaN interface exhibited the greatest elastic modulus (473 ± 26 GPa) and stiffness (0.76 ± 0.13 mN/nm).

Savchenko, N. L. et al. Adaptation and self-healing effect of tribo-oxidizing in high-speed sliding friction on ceramic composite ZrB2-SiC. Wear https://doi.org/10.1016/j.wear.2020.203204 (2020).

Article Google Scholar

Li, M., Ke, C. & Zhang, J. Synthesis of ZrB2 powders by molten-salt participating silicothermic reduction. J. Alloys Compd. 834, 155062. https://doi.org/10.1016/j.jallcom.2020.155062 (2020).

Article CAS Google Scholar

Fattahi, M. et al. Nano-diamond reinforced ZrB2–SiC composites. Ceram. Int. https://doi.org/10.1016/j.ceramint.2020.01.008 (2020).

Article Google Scholar

Jafari, S., Bavand-Vandchali, M., Mashhadi, M. & Nemati, A. Effects of HfB2 addition on pressureless sintering behavior and microstructure of ZrB2-SiC composites. Int. J. Refract. Met. Hard Mater. 94, 105371. https://doi.org/10.1016/j.ijrmhm.2020.105371 (2021).

Article CAS Google Scholar

Ivor, M. et al. Nanoindentation and tribology of ZrB2 based luminescent ceramics. J. Eur. Ceram. Soc. 40, 4901–4908. https://doi.org/10.1016/j.jeurceramsoc.2020.03.021 (2020).

Article CAS Google Scholar

Mungiguerra, S. et al. Improved aero-thermal resistance capabilities of ZrB2-based ceramics in hypersonic environment for increasing SiC content. Corros. Sci. 178, 109067. https://doi.org/10.1016/j.corsci.2020.109067 (2021).

Article CAS Google Scholar

Mungiguerra, S. et al. Ultra-high-temperature testing of sintered ZrB2-based ceramic composites in atmospheric re-entry environment. Int. J. Heat Mass Transf. 156, 119910. https://doi.org/10.1016/j.ijheatmasstransfer.2020.119910 (2020).

Article CAS Google Scholar

Kashyap, S. K. & Mitra, R. Densification behavior involving creep during spark plasma sintering of ZrB2-SiC based ultra-high temperature ceramic composites. Ceram. Int. 46, 5028–5036. https://doi.org/10.1016/j.ceramint.2019.10.246 (2020).

Article CAS Google Scholar

Hassan, R. & Balani, K. Oxidation kinetics of ZrB2-and HfB2-powders and their SiC reinforced composites. Corros. Sci. 177, 109024. https://doi.org/10.1016/j.corsci.2020.109024 (2020).

Article CAS Google Scholar

Rezapour, A. & Balak, Z. Fracture toughness and hardness investigation in ZrB2–SiC–ZrC composite. Mater. Chem. Phys. 241, 122284. https://doi.org/10.1016/j.matchemphys.2019.122284 (2020).

Article CAS Google Scholar

Nguyen, T. P. et al. Electron microscopy investigation of spark plasma sintered ZrO2 added ZrB2–SiC composite. Ceram. Int. 46, 19646–19649. https://doi.org/10.1016/j.ceramint.2020.04.292 (2020).

Article CAS Google Scholar

Hassan, R., Kundu, R. & Balani, K. Oxidation behaviour of coarse and fine SiC reinforced ZrB2 at re-entry and atmospheric oxygen pressures. Ceram. Int. https://doi.org/10.1016/j.ceramint.2020.01.125 (2020).

Article Google Scholar

Song, S. et al. In situ fabrication of ZrB2-SiC composite powders with controllable morphology by a two-step calcination method. J. Solid State Chem. 273, 101–105. https://doi.org/10.1016/j.jssc.2019.02.042 (2019).

Article ADS CAS Google Scholar

Popov, O., Vleugels, J., Zeynalov, E. & Vishnyakov, V. Reactive hot pressing route for dense ZrB2-SiC and ZrB2-SiC-CNT ultra-high temperature ceramics. J. Eur. Ceram. Soc. 40, 5012–5019. https://doi.org/10.1016/j.jeurceramsoc.2020.07.039 (2020).

Article CAS Google Scholar

Sun, S. et al. Fabrication of ZrB2-SiC powder with a eutectic phase for sintering or plasma spraying. Powder Technol. 372, 506–518. https://doi.org/10.1016/j.powtec.2020.06.019 (2020).

Article CAS Google Scholar

Nguyen, T. P. et al. Influence of SiAlON addition on the microstructure development of hot-pressed ZrB2–SiC composites. Ceram. Int. 46, 19209–19216. https://doi.org/10.1016/j.ceramint.2020.04.258 (2020).

Article CAS Google Scholar

Emdadi, A., Watts, J., Fahrenholtz, W. G., Hilmas, G. E. & Zaeem, M. A. Predicting effective fracture toughness of ZrB2-based ultra-high temperature ceramics by phase-field modeling. Mater. Des. https://doi.org/10.1016/j.matdes.2020.108713 (2020).

Article Google Scholar

AkbarpourShalmani, S. A., Sobhani, M., Mirzaee, O. & Zakeri, M. Effect of HfB2 and WC additives on the ablation resistance of ZrB2–SiC composite coating manufactured by SPS. Ceram. Int. 46, 25106–25112. https://doi.org/10.1016/j.ceramint.2020.06.297 (2020).

Article CAS Google Scholar

Xia, C. et al. Enhanced fracture toughness of ZrB2–SiCw ceramics with graphene nano-platelets. Ceram. Int. 46, 24906–24915. https://doi.org/10.1016/j.ceramint.2020.06.275 (2020).

Article CAS Google Scholar

Zamora, V., Guiberteau, F. & Ortiz, A. L. Effect of high-energy ball-milling on the spark plasma sinterability of ZrB2 with transition metal disilicides. J. Eur. Ceram. Soc. 40, 5020–5028. https://doi.org/10.1016/j.jeurceramsoc.2020.06.046 (2020).

Article CAS Google Scholar

Delbari, S. A., Sabahi Namini, A. & Shahedi, A. M. Hybrid Ti matrix composites with TiB2 and TiC compounds. Mater Today Commun. 20, 100576. https://doi.org/10.1016/j.mtcomm.2019.100576 (2019).

Article CAS Google Scholar

Fattahi, M. et al. Strengthening of TiC ceramics sintered by spark plasma via nano-graphite addition. Ceram. Int. https://doi.org/10.1016/j.ceramint.2020.01.291 (2020).

Article Google Scholar

Fattahi, M. et al. Characterization of triplet Ti–TiB–TiC composites: Comparison of in-situ formation and ex-situ addition of TiC. Ceram. Int. https://doi.org/10.1016/j.ceramint.2020.01.204 (2020).

Article Google Scholar

Xia, C. et al. Electron microscopy study of ZrB2–SiC–AlN composites: Hot-pressing vs. pressureless sintering. Ceram. Int. https://doi.org/10.1016/j.ceramint.2020.08.054 (2020).

Article Google Scholar

Nguyen, V.-H. et al. Role of hot-pressing temperature on densification and microstructure of ZrB2–SiC ultrahigh temperature ceramics. Int. J. Refract. Met. Hard Mater. https://doi.org/10.1016/j.ijrmhm.2020.105355 (2020).

Article Google Scholar

Wu, W. W., Estili, M., Nishimura, T., Zhang, G. J. & Sakka, Y. Machinable ZrB2-SiC-BN composites fabricated by reactive spark plasma sintering. Mater. Sci. Eng. A 582, 41–46. https://doi.org/10.1016/j.msea.2013.05.079 (2013).

Article CAS Google Scholar

Nguyen, V.-H. et al. TEM characterization of hot-pressed ZrB2-SiC-AlN composites. Results Phys. https://doi.org/10.1016/j.rinp.2020.103348 (2020).

Article Google Scholar

Ahmadi, Z., Nayebi, B., Shahedi Asl, M., GhassemiKakroudi, M. & Farahbakhsh, I. Sintering behavior of ZrB2–SiC composites doped with Si3N4: A fractographical approach. Ceram. Int. 43, 9699–9708. https://doi.org/10.1016/j.ceramint.2017.04.144 (2017).

Article CAS Google Scholar

Karimirad, S. & Balak, Z. Characteristics of spark plasma sintered ZrB2-SiC-SCFs composites. Ceram. Int. 45, 6275–6281. https://doi.org/10.1016/j.ceramint.2018.12.109 (2019).

Article CAS Google Scholar

Balak, Z. & Zakeri, M. Effect of HfB2 on microstructure and mechanical properties of ZrB2-SiC-based composites. Int. J. Refract. Met. Hard Mater. 54, 127–137. https://doi.org/10.1016/j.ijrmhm.2015.07.011 (2016).

Article CAS Google Scholar

Kavakeb, K., Balak, Z. & Kafashan, H. Densification and flexural strength of ZrB2–30 vol% SiC with different amount of HfB2. Int. J. Refract. Met. Hard Mater. https://doi.org/10.1016/j.ijrmhm.2019.104971 (2019).

Article Google Scholar

Balak, Z. & Zakeri, M. Application of Taguchi L32 orthogonal design to optimize flexural strength of ZrB2-based composites prepared by spark plasma sintering. Int. J. Refract. Met. Hard Mater. 55, 58–67. https://doi.org/10.1016/j.ijrmhm.2015.11.009 (2016).

Article CAS Google Scholar

Eatemadi, R. & Balak, Z. Investigating the effect of SPS parameters on densification and fracture toughness of ZrB2-SiC nanocomposite. Ceram. Int. 45, 4763–4770. https://doi.org/10.1016/j.ceramint.2018.11.169 (2019).

Article CAS Google Scholar

Balak, Z., Azizieh, M., Kafashan, H., Asl, M. S. & Ahmadi, Z. Optimization of effective parameters on thermal shock resistance of ZrB2-SiC-based composites prepared by SPS: Using Taguchi design. Mater. Chem. Phys. 196, 333–340. https://doi.org/10.1016/j.matchemphys.2017.04.062 (2017).

Article CAS Google Scholar

Vaziri, P. & Balak, Z. Improved mechanical properties of ZrB2-30 vol% SiC using zirconium carbide additive. Int. J. Refract. Met. Hard Mater. 83, 104958. https://doi.org/10.1016/j.ijrmhm.2019.05.004 (2019).

Article CAS Google Scholar

Balak, Z. Shrinkage, hardness and fracture toughness of ternary ZrB2–SiC-HfB2 composite with different amount of HfB2. Mater. Chem. Phys. 235, 121706. https://doi.org/10.1016/j.matchemphys.2019.05.094 (2019).

Article ADS CAS Google Scholar

Balak, Z., Zakeri, M., Rahimipour, M. & Salahi, E. Taguchi design and hardness optimization of ZrB2-based composites reinforced with chopped carbon fiber and different additives and prepared by SPS. J. Alloys Compd. 639, 617–625. https://doi.org/10.1016/j.jallcom.2015.03.131 (2015).

Article CAS Google Scholar

Nasiri, Z. & Mashhadi, M. Microstructure and mechanical behavior of ternary phase ZrB2-SiC-AlN nanocomposite. Int. J. Refract. Met. Hard Mater. 78, 186–192. https://doi.org/10.1016/j.ijrmhm.2018.09.009 (2019).

Article CAS Google Scholar

Zhang, C. J. et al. Temperature dependence of tensile properties and fracture behavior of as rolled TiB/Ti composite sheet. Mater. Sci. Eng. A 556, 962–969. https://doi.org/10.1016/j.msea.2012.07.110 (2012).

Article CAS Google Scholar

Gorsse, S., Petitcorps, Y. L., Matar, S. & Rebillat, F. Investigation of the Young’s modulus of TiB needles in situ produced in titanium matrix composite. Mater. Sci. Eng. A 340, 80–87. https://doi.org/10.1016/S0921-5093(02)00188-0 (2003).

Article Google Scholar

Hynowska, A. et al. Nanostructured β-phase Ti–31.0Fe–9.0Sn and sub-μm structured Ti–39.3Nb–13.3Zr–10.7Ta alloys for biomedical applications: Microstructure benefits on the mechanical and corrosion performances. Mater. Sci. Eng. C 32, 2418–2425. https://doi.org/10.1016/j.msec.2012.07.016 (2012).

Article CAS Google Scholar

Bao, Y. W., Wang, W. & Zhou, Y. C. Investigation of the relationship between elastic modulus and hardness based on depth-sensing indentation measurements. Acta Mater. 52, 5397–5404. https://doi.org/10.1016/j.actamat.2004.08.002 (2004).

Article ADS CAS Google Scholar

Musil, J., Kunc, F., Zeman, H. & Poláková, H. Relationships between hardness, Young’s modulus and elastic recovery in hard nanocomposite coatings. Surf. Coat. Technol. 154, 304–313. https://doi.org/10.1016/S0257-8972(01)01714-5 (2002).

Article CAS Google Scholar

Download references

This research was supported by National Research Foundation of Korea (NRF) funded by the Ministry of Science and ICT (2018M3A9H102314121, 2020H1D3A1A04081409, 2020M2D8A206983011, 2021R1A4A3027878, 2020M2D8A1066203, and 2022R111A1A0106757211). The financial supports of the Basic Science Research Program (2017R1A2B3009135) through the National Research Foundation of Korea is also appreciated. Furthermore, this work was carried out with the support of the Cooperative Research Program for Agriculture Science and Technology Development (Project No. PJ01706702) Rural Development Administration, Republic of Korea.

Department of Engineering Sciences, Faculty of Advanced Technologies, University of Mohaghegh Ardabili, Ardabil, Iran

Seyed Ali Delbari & Abbas Sabahi Namini

Department of Materials Science and Engineering, Research Institute of Advanced Materials, Seoul National University, Seoul, 08826, Republic of Korea

Seonyong Lee, Jinghan Wang, Ho Won Jang & Mohammadreza Shokouhimehr

Advanced Nano Surface Department, Korea Institute of Materials Science, Changwon, 51508, Republic of Korea

Sunghoon Jung

Division of Powder/Ceramics Research, Korea Institute of Materials Science, Changwon, 51508, Republic of Korea

Sea-Hoon Lee

Innovative Enterprise Cooperation Center, Korea Institute of Science & Technology, Hwarangro 14-gil, Seongbuk-gu, Seoul, Republic of Korea

Joo Hwan Cha

Department of Materials Science and Engineering, Institute of Green Manufacturing Technology, Korea University, 145, Anam-ro Seongbuk-gu, Seoul, 02841, South Korea

Jin Hyuk Cho & Soo Young Kim

You can also search for this author in PubMed Google Scholar

M.S., A.S.N., and S.Y.K. designed and conceived the idea. S.J.L., S.H.L., S.A.D., J.H.C., and J.H.C. prepared the samples. S.J.L., S.H.L., S.A.D., J.H.C., J.W., S.L., and M.S. assisted the analyses and characterizations. A.S.N., H.W.J., S.Y.K., and M.S. developed the project and revised the manuscript. A.S.N., S.Y.K., and M.S. supervised the project. All authors contributed in scientific discussions and preparing the manuscript.

Correspondence to Abbas Sabahi Namini, Soo Young Kim or Mohammadreza Shokouhimehr.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Delbari, S.A., Namini, A.S., Lee, S. et al. Microstructural and nanoindentation study of TaN incorporated ZrB2 and ZrB2–SiC ceramics. Sci Rep 12, 13765 (2022). https://doi.org/10.1038/s41598-022-17797-6

Download citation

Received: 08 December 2021

Accepted: 31 July 2022

Published: 12 August 2022

DOI: https://doi.org/10.1038/s41598-022-17797-6

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Blog

Microstructural and nanoindentation study of TaN incorporated ZrB2 and ZrB2